Products > Pipeline Coatings > 3ply tape T400 > Polyethylene 3ply Tape(T 400 )
Product name : Polyethylene 3ply Tape(T 400 )
Item : 20137111131
Thickness : 
Product Name : 
UV resistance : 
Adhesive : 
Backing Film : 
Roll size  : 
Delivery Time  : 
Min Order  : 
Similar Brand  : 
Usage  : 
 Enlarge Image                   Back
←[Previous Product]              [Next Product]→


Polyethylene 3ply Tape

Excellent bonding between adhesive and carrier film via co-extruded intermediate layer.
Mechanically highly resistant tape system.
Practically impermeable to water vapour and oxygen.
Resistant to soil bacterial and soil electrolyte.
Compatible with coating from PE,PP,FBE,PU,CTE and Bitumen and ext…
High adhesion and shear resistance
Resistance to corrosion disbondment
High electrical resistance
High dielectric strength
High corrosion protection for steel substrates
Tensile strength N/cm 67
Elongation at break % 450
Peel strength to pipe surface at 23 ℃
at 50℃ N/cm
Peel strength tape to tape at 23 ℃ at 50℃ N/cm
Dielectric strength Kv/mm 32
Insulation Resistance Ohm.m² 1012
Water Vapor Transmission g/ m2 /24h 0.1
Brittleness temperature ℃ -46±4
Water Absorption % 0.1 max
Impact resistance at 23° J 18
Cathodic disbandment at 23°c
at 50°c mm 15
Lap shear strength at 50℃ N/mm2 0.05

Asymmetrically structured three-ply plastics tape consisting of a stabilized polyethylene backing with plastic butyl rubber on both sides. The consistency of the butyl rubber on the one side facing the pipe surface should be formulated in such a way that, under tension, it flows on uneven steel surfaces. To facilitate correct application this butyl layer should be of a black color. The grey butyl layer of the tape must face the steel and this should always be the thicker layer of butyl rubber.
In order to avoid delaminating tape must contain co-extruded intermediate layers.

The tape must be fully compatible with the properties of the primer. The tape must be self-amalgamating between the layers and at the overlaps and must have a release paper or film.

Two-ply plastics tape consisting of a stabilized high density polyethylene backing with plastic butyl rubber on one side. The outer wrap tape must be fully compatible with the properties of the inner wrap. The outer wrap must fully self-amalgamate with the inner wrap tape at contact areas.
In order to avoid delaminating between carrier film and butyl rubber, tape should contain co-extruded intermediate layers.

Related Products :
altene alta tp1822.30 double sided adhesive tape for pipeline anti corrosion
altene alta tp1822.30 double sided adhesive tape for pipeline anti corrosion
Oil gas pipeline bitumen tape T400
Oil gas pipeline bitumen tape T400
Double Sides anticorrosion Tape , 3ply PE tape
Double Sides anticorrosion Tape , 3ply PE tape
Polyethylene 3ply Tape(T 400 )
Polyethylene 3ply Tape(T 400 )
Polyethylene 3ply Tape for Pipelines
Polyethylene 3ply Tape for Pipelines